Zirconia bụ klas dị mkpa nke ihe seramiiki dị ka seramiki dị elu, ọ bụkwa ihe dị mkpa dị mkpa maka mmepe nke ụlọ ọrụ ọgbara ọhụrụ.Zirconia ceramics, nke nwere nnukwu agbaze na ebe a na-esi esi mmiri, ike siri ike, nkwụsi ike dị oke mma, dị ka ihe mkpuchi na ụlọ okpomọkụ, na okpomọkụ dị elu nwere ihe ndị magburu onwe ya dị ka eletriki eletrik. ndu anyi.Mpaghara ọrụ gụnyere: nkwukọrịta 5G, petrochemical, akụrụngwa ahụike, ụlọ ọrụ fotovoltaic, ikuku ikuku, akụrụngwa agha, semiconductor, ngwa eletrọnịkị, nfuli, valves, batrị lithium, wdg.
Njirimara na njirimara nke ceramics zirconia
Zirconia ceramics bụ ụdị ọhụrụ nke ceramics nke teknụzụ dị elu, ya na mgbakwunye na ike dị elu, ike siri ike, nguzogide okpomọkụ dị elu, acid na alkali corrosion resistance na elu chemical kwụsie ike na ọnọdụ ndị ọzọ, n'otu oge ahụ na ọkọ na-eguzogide ma na-eyi nguzogide, ọ dịghị. ihe nchebe mgbaama, arụmọrụ ikpo ọkụ dị mma na njirimara ndị ọzọ, ebe ike machinability siri ike, mmetụta dị mma.
1, ebe mgbaze dị elu, ebe mgbaze dị elu na inertness kemịkalụ na-eme zirconia nwere ike iji mee ihe dị ka mma refractory;
2, na nnukwu ike ike na mma iyi mgbochi;
3, ike na ike dịtụ ukwuu;
4, obere conductivity thermal, ọnụ ọgụgụ mgbasawanye dị ala, dabara adaba maka ihe seramiiki nhazi;
5, ịrụ ọrụ eletrik dị mma, site na nchepụta arụmọrụ nchekwa, seramiiki zirconia dị ka ihe na-abụghị ọla enweghị mmetụta mkpuchi na akara electromagnetic, agaghị emetụta nhazi antenna n'ime.
Nka nka | ||
Ihe oru ngo | Nkeji | Ọnụọgụ ọnụọgụgụ |
Ihe onwunwe | / | ZrO2 95% |
Agba | / | Ọcha |
Njupụta | g/cm3 | 6.02 |
Ike Flexural | MPa | 1,250 |
Ike mkpakọ | MPa | 5,690 |
Modul nke Young | GPA | 210 |
Mmetụta Mmetụta | MPa m1/2 | 6-7 |
Weibull ọnụ ala | m | 10 |
Vickers ike ike | HV 0.5 | 1,800 |
(ọnụọgụ Mgbasawanye okpomọkụ) | 1n-5k-1 | 10 |
Nrụpụta okpomọkụ | W/mK | 一 |
Thermal Shock kwụsie ike | △T°C | 一 |
Okpomọkụ ojiji kacha | Celsius C | 一 |
20°C Mgbochi olu | Ωcm | 一 |
Ike Dielectric | kV/mm | 一 |
Dielectric Constant | εr | 一 |